Bone repair material

ABSTRACT

The bone repair material comprises the following components: 
     A) a first granular component with a diameter larger than 20 μm chosen from the group of: calcium phosphate, calcium pyrophosphate, or calcium sulfate dihydrate; 
     B) a second component chosen from the group of apatite powder with a particle diameter smaller than 1 μm, (preferably smaller than 100 nm); and 
     B) a third component comprising water or an aqueous solution, whereby 
     C) the volume fraction of the second and third component represents at least 35 volume-% of the total bone repair material.

BACKGROUND OF INVENTION

1. Field of Invention

The invention relates to a bone repair material that is useful in the repair of bone defects, in particular in the repair of defects filled with aqueous body fluids such as blood.

2. Description of Related Art

From WO03/082365 a kneadable and formable bone replacement mass is known based on ceramic particles having a diameter in the range of 0.1 mm to 5.6 mm suspended in a hydrogel. This mass has the disadvantage that hydrogels for human use are very expensive. Another disadvantage connected with hydrogels is the fact that sterilization via gamma-irradiation destroys the polymer chain, hence reducing the average molecular weight and decreasing the polymer viscosity.

From the WO 99/20237 a stomatic composition based on hydroxyapatite nanoparticles is known which may include further components such as various abrasive materials (0 to 25%). These abrasive materials may consist of anhydrous dicalcium phosphate, dicalcium phosphate dihydrate, and calcium carbonate. However, there is no indication in this prior art document about the preferred size range for these abrasive materials. Also it does not mention the use of β-tricalcium phosphate. Moreover, this prior art cement is proposed only for use in the field of stomatology and not of bone repair. The main disadvantage of this known material is that it does not allow the surrounding bone cells to anchor and to proliferate.

From two articles of JJC Arts et al.:

-   -   “The use of a bioresorbable nano-crystalline hydroxyapatite         paste in acetabular bone impaction grafting”. Biomaterials, In         Press, and     -   “Cemented cup stability during lever-out testing after         acetabular bone impaction grafting with bone graft substitutes         mixes containing morselized cancellous bone and tricalcium         phosphate-hydroxyapatite granules” published in Proc Inst Mech         Eng [H] 2005;219:257-67, it is known that a nano-crystalline         paste (40 weight-% water) can be combined with biphasic calcium         phosphate granules (80% β-TCP, 20% HA). The latter authors used         very large granule diameters, i.e. 1.5-2.0 mm, 4-6 mm, and 4-8         mm granules combined with a very small nano-crystalline paste         content (up to 33 volume-%), because they wanted to use the         granular paste for impaction grafting. Results showed however         that a 33 volume-% paste content—for that special field of         application—was too much to provide an adequate initial cup         stability and therefore the authors were led to prefer lower         contents in the region of 10% for the nano-crystalline paste.         For these reasons the authors did not even consider the         possibility of using a higher content (over the 33 volume-%) of         nano-crystalline paste.

Accordingly, it is the principal object of the present invention to provide a bone repair material overcoming the above disadvantages and not being based on hydrogel.

BRIEF SUMMARY OF THE INVENTION

To achieve the above object the present invention relates to a cement comprising:

-   -   A) a first granular component having a diameter larger than 20         μm selected from the group consisting of: calcium phosphate,         calcium pyrophosphate and calcium sulfate dihydrate;     -   B) a second component consisting of apatite powder having a         particle diameter smaller than 1 μm; and     -   C) a third component comprising water or an aqueous solution;         whereby     -   D) the second component and the third component collectively         represent at least 35 volume-% of the total bone repair         material.

The advantages of the bone repair material according to the invention compared to the state of the art materials are the following:

-   -   compared to hydrogel-based putties they are much cheaper because         there is no need to use an expensive hydrogel for human use;     -   compared to pure nanoparticle-liquid mixtures they offer the         important advantage that the additional, comparatively large         granules provide a scaffold on which bone cells can anchor and         proliferate;     -   compared to the usual calcium phosphate cements (pastes/putties         that harden within a short time after mixing fluid and powder         components), the bone repair material according to the invention         is much easier to use (no time-dependent properties) and to         produce (relatively inert); and     -   the bone repair material (with no hydrogel present) can be         sterilized without any problem by gamma irradiation.

DETAILED DESCRIPTION OF THE INVENTION

The first component can be chosen from the group of β-tricalcium phosphate, α-tricalcium phosphate, hydroxyapatite, tetracalcium phosphate, DCPD [dicalcium phosphate dihydrate (CaHPO₄.2H₂O)], DCP [dicalcium phosphate (CaHPO₄)], OCP [octocalcium phosphate (Ca₈H₂(PO₄)₆.5H₂O)], α-CPP [α-calcium pyrophosphate (Ca₂P₂O₇)], β-CPP [β-calcium pyrophosphate (Ca₂P₂O₇)], γ-CPP [γ-calcium pyrophosphate (Ca₂P₂O₇)], and CSD [calcium sulfate dihydrate (CaSO₄.2H₂O)]. Concerning these different compounds, the advantage of choosing specific compounds is the fact that the resorption rate of the paste can be modulated according to the clinical indication. For example, CSD is rapidly cleared from the body, whereas sintered hydroxyapatite particles would remain unresorbed for decades.

The diameter of the first granular component is typically larger than 50 microns and preferably larger than 100 microns. It is typically smaller than 1000 microns and preferably smaller than 200 microns.

In a special embodiment the fraction of the second and third component is in the range of 77 to 83 volume-% of the total bone repair material. If lower ratios are used (below 77%), the cement mixture becomes too brittle. If higher ratios are used (close to 83%) the cement mixture becomes elastic, moldable and well injectable.

The apatite powder may be chosen from the group of calcium-deficient hydroxyapatite, hydroxyapatite or fluoroapatite.

The first component comprises preferably a mixture of granules of different size, preferably in the form of several fractions of monodispersed granules. The size ratio of two neighboring size fractions should be larger than 1.4, preferably larger than 1.5.

In a further embodiment the granules of the first component are macroporous, preferably with a pore diameter superior to 0.05 mm. The advantage lies in the optimization of the mechanical and biological properties of the granules.

In a further embodiment the granules of the first component have a porosity of less than 90%. Higher porosities would lead to an undesirable granule fracturing during handling.

Typically the granules of said first component have an apparent volume smaller than 80%, preferably smaller than 30%. 80% meaning that the material volume “mv” present in a defect of volume “dv” corresponds to less than 80% of “dv”. The volume of the material “mv” is calculated by dividing the material weight by the theoretical density of the material. Typically the apparent volume may be close 25%.

In a special embodiment the granules of the first component are spherical. In an other embodiment the granules of the first component are non-spherical and preferably concave. The advantage of the latter embodiment is that cells can more easily proliferate in concavities than convexities.

In a further embodiment the apatite powder comprises deagglomerated powder particles. Apatite powders are typically obtained by precipitation. Therefore, any precipitation method that enables the obtention of deagglomerated particles is of interest. The use of a nano- or micro-batch reactor (precipitation in a nano- or micro-volume) are of interest.

In a further embodiment the ratio between the third component expressed in milliliters and the sum of said first and second components expressed in grams is comprised in the range of 0.05 to 1.0 mL/g, preferably in the range of 0.1 to 0.7 mLg. The volume ratio between the third and the first component may be in the range of 2.7-3.8 preferably between 3.0-3.4.

The bone repair material may further comprise an additive increasing the surface charge of the particles present in the formulation. Such additives may include a carboxylated compound, preferably having citrate or poly(carboxylated) ions, e.g. polyacrylic acid.

In a further embodiment the third component has a high ionic strength, typically 0.15 m or higher. This reduces the thickness of the electrical double layer present on the particle surface, hence reducing the repulsive interactions between the particles and hence increasing the stickiness of the resulting paste.

In a further embodiment the third component comprises a content of 0.1-1.0 w % of a hydrogel, preferably sodium hyaluronate.

The bone repair material may further comprise one or more drugs useful in the treatment of bone defects or bone diseases, in particular pharmaceutically or physiologically active substances. Specific examples would include antibacterial substances, anti-inflammatory drugs, drugs against osteoporosis, anti-cancer drugs, peptides, proteins, trophic factors and substances promoting bone growth, in particular growth factors and bone morphogenetic proteins.

The bone repair material further comprise an inorganic inhibitor for apatite dissolution and growth, preferably in the form of magnesium or pyrophosphate ions. The advantage is a stabilization of the formulation which prolongs its shelf life.

The bone repair material may further comprise an organic inhibitor for apatite dissolution and growth, preferably in the form of citrate ions, amino acids, peptides or proteins.

The bone repair material may be formulated in the form of a ready mixed putty material.

In a further embodiment the first and second component are in the form of a dry mixture to which the third component is to be added before use.

The third component may comprise blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells.

In a further embodiment the second and third component are in the form of a nanocrystalline paste to which the first component is admixed before use.

In a further embodiment the third component comprises partly or fully a fluid extracted from the patient without or with additional processing, preferably in the form of blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells.

The third component may comprise cells with osteogenic potential that have been cultivated and/or differentiated prior to their use. Said cells may be embryonic stem cells, stem cells, bone marrow cells or osteoblasts.

The bone repair may further comprise a radiopacifier. The radiopacifier may be in a liquid or in a solid form. Examples of powders are barium sulfate, strontium carbonate, zirconium oxide, bismuth oxide, metallic powders such as Tantalum, Tungsten, Gold, Platinum, or Titanium. Examples of liquids are liquids containing iode-based organic compounds such as: lopamidol, lodixalonum, lopentol, lopramidum and lotralonum.

The bone repair material according to the invention may be used for the preparation of an agent for the treatment of osteoporosis or bone tumors.

The mixture of the bone repair material may prepared directly in the operating room.

A further use of the bone repair material according to the invention consists in that blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells are admixed as third component to a mixture of said first and second component. The main purpose of that use would be a putty material to be used as a bone repair material, i.e. to fill bone defects.

Preferably, the amount of liquid should be chosen in such a way that the amount of liquid can fill up all the gaps present within the powder and the granules. For example, if the apparent density of a mixture of β-TCP powder and dense granules is 0.8 g/cc, the amount of liquid that has to be added should be close to (3.1-0.8)/3.1=0.74 mL per gram of powder/granule mixture (3.1 g/cc is the absolute density of β-TCP). If the amount of liquid is lower than this ideal amount, the mixture is very brittle. If the amount of liquid is slightly larger than the ideal amount, the mixture becomes elastic, moldable, injectable, and sticky.

The useful amount of powder depends very much on the properties that the paste should have. Generally, an increase of the powder/granule ratio increases the elasticity, mouldability and injectability of the paste (keeping enough aqueous solution in the mixture, as described above for the preferred amount of liquid). So, preferably a balance should be found between good biological properties (enough granules to support cell anchorage and proliferation) and good paste properties (mouldability, elasticity, injectability).

Further objects and advantages of the invention will become apparent from the following specific examples.

EXAMPLES Example 1

Several pastes were produced to investigate the effect of the content of the various components on the properties of the paste. The pastes were produced by mixing tricalcium phosphate powder with β3-TCP granules, and demineralized water. The tricalcium phosphate powder had a plastic limit of 1.01 mL water per gram of powder. The β-TCP granules had a diameter in the range of 0.180 and 0.5 mm (50% between 0.18 and 0.25 mm and 50% between 0.355 and 0.5 mm) and had an apparent density of 0.68-0.79 g/cc (depending on the granule size; a given amount of particles was packed in a graduated cylinder—the particle weight was divided by the apparent volume to determine the apparent density). The various compositions tested here are shown in Table 1.

The pastes were characterized by several means: stickiness (ability to stick to a surface), mouldability (ability to be shaped), and injectability (ability to be injected through a syringe). Additionally, the pastes were tested qualitatively by several people.

All 6 pastes had a similar stickiness and mouldability. However, pastes with more powder (samples 1-4 to 1-6) were injectable contrary to the paste with less powder (samples 1-1 to 1-3) which were not injectable at all. By hand, the paste with the largest amount of granule felt granular, whereas the other pastes were rather smooth.

TABLE 1 composition of the pastes obtained with tricalcium phosphate powder, β-TCP granules, and demineralized water. Paste Powder Granules Liquid # [g] [g] [mL] 1-1 2.00 2.15 2.00 (20.0%) (20.6%) (59.4%) 1-2 2.00 2.35 2.20 (18.6%) (20.9%) (60.5%) 1-3 2.00 2.55 2.40 (17.3%) (21.1%) (61.6%) 1-4 2.00 1.92 2.00 (20.5%) (18.8%) (60.7%) 1-5 2.00 2.09 2.20 (19.0%) (19.0%) (62.0%) 1-6 2.00 2.27 2.40 (17.8%) (19.2%) (63.0%) The volume fraction (based on the weight and the theoretical density of each component) is given within parenthesis.

Example 2

The same powders and granules as those used in example 1 were used in this example. The paste was produced by combining a sterile mixture of 2 g tricalcium phosphate powder and 2.27 g β-TCP granules with 2.4 mL of human blood. The three components were mixed in a bowl with a spatula during one minute. The resulting paste was then moulded by hand and implanted into a model defect.

Example 3

Several pastes were produced to investigate the effect of the content of the various components on the properties of the paste. The pastes were produced by mixing tricalcium phosphate powder with β-TCP granules, and an aqueous magnesium chloride solution. The tricalcium phosphate powder had a plastic limit of 1.01 mL water per gram of powder. The β-TCP spherical granules had a diameter of 0.25-0.35 mm, and had an apparent density of 1.7-1.9 g/cc. All mixtures had a good mouldability, a low stickiness, and a good injectability. All mixtures felt very “granular” in the fingers.

TABLE 2 composition of the pastes obtained with tricalcium phosphate, β-TCP spherical granules and demineralized water. Paste Powder Granules Liquid # [g] [g] [mL] 2-1 2.0 12.5 2.0 (10.2%) (60.0%) (29.8%) 2-2 2.0 13.4 2.2  (9.4%) (60.0%) (30.6%) 2-3 2.0 14.3 2.4  (8.8%) (60.0%) (31.2%) 2-4 2.0 10.6 2.0 (11.1%) (56.1%) (32.8%) 2-5 2.0 11.4 2.2 (10.3%) (56.1%) (33.6%) 2-6 2.0 12.2 2.4  (9.7%) (56.1%) (34.2%) The volume fraction (based on the weight and the theoretical density of each component) is given within parenthesis.

For the laboratory examples a spatula and a beaker were use for mixing the components. For production purposes mixing machines known in the art would be used. For those products which would be offered to the surgeon for mixing with blood an adequate mixing device could be added to a suitable package. 

1. A bone repair material comprising A) a first granular component with a diameter larger than 20 μm chosen from the group of calcium phosphate, calcium pyrophosphate, or calcium sulfate dihydrate; B) a second component with a particle diameter smaller than 1 μm chosen from the group of calcium-deficient hydroxyapatite, hydroxyapatite or fluoroapatite; and C) a third component comprising water or an aqueous solution, whereby p1 D) the volume fraction of the second and third component represents at least 35 volume-% of the total bone repair material; and E) the volume ratio between the third and the first component is in the range of 2,7-3,8.
 2. Bone repair material according to claim 1, characterized in that the first component is chosen from the group of β-tricalcium phosphate, α-tricalcium phosphate, hydroxyapatite, tetracalcium phosphate, DCPD [dicalcium phosphate dihydrate (CaHPO₄.2H₂O)], DCP [dicalcium phosphate (CaHPO₄)], OCP [octocalcium phosphate (Ca₈H₂(PO₄)₆.5H₂O)], α-CPP [α-calcium pyrophosphate (Ca₂P₂O₇)], β-CPP [β-calcium pyrophosphate (Ca₂P₂O₇)], γ-CPP [γ-calcium pyrophosphate (Ca₂P₂O₇)], and CSD [calcium sulfate dihydrate (CaSO₄.2H₂O)].
 3. Bone repair material according to claim 1 or 2, characterized in that the diameter of said first granular component is larger than 50 microns, preferably larger than 100 microns.
 4. Bone repair material according to one of the claims 1 to 3, characterized in that the diameter of said first granular component is smaller than 1000 microns, preferably smaller than 200 microns.
 5. Bone repair material according to one of the claims 1 to 4, characterized in that the fraction of the second and third component is in the range of 77 to 83 volume-% of the total bone repair material.
 6. Bone repair material according to one of the claims 1 to 5, characterized in that the said second component has a particle diameter smaller than 100 nm.
 7. Bone repair material according to one of the claims 1 to 6, characterized in that the first component comprises a mixture of granules of different size, preferably in the form of several fractions of monodispersed granules.
 8. Bone repair material according to claim 7, characterized in that the size ratio of two neighboring size fractions are larger than 1,4, preferably larger than 1,5.
 9. Bone repair material according to one of the claims 1 to 8, characterized in that the granules of the first component are macroporous, preferably with a pore diameter superior to 0,05 mm.
 10. Bone repair material according to one of the claims 1 to 9, characterized in that the granules of the first component have a porosity of less than 90%.
 11. Bone repair material according to one of the claims 1 to 10, characterized in that said granules of said first component have an apparent volume smaller than 80%, preferably smaller than 30%.
 12. Bone repair material according to one of the claims 1 to 11, characterized in that the granules of the first component are spherical.
 13. Bone repair material according to one of the claims 1 to 11, characterized in that the granules of the first component are non-spherical and preferably concave.
 14. Bone repair material according to one of the claims 1 to 13, characterized in that the apatite powder comprises deagglomerated powder particles.
 15. Bone repair material according to one of the claims 1 to 14, characterized in that the ratio between said third component expressed in milliliters and the sum of said first and second components expressed in grams is comprised in the range of 0.05 to 1.0 mL/g, preferably in the range of 0.1 to 0.7 mL/g.
 16. Bone repair material according to one of the claims 1 to 15, characterized in that the volume ratio between the third and the first component is in the range of 3.0 to 3.4.
 17. Bone repair material according to one of the claims 1 to 16, characterized in that it further comprises an additive increasing the surface charge of the particles present in the formulation.
 18. Bone repair material according to claim 17, characterized in that said additive is a carboxylated compound, preferably having citrate or poly(carboxylated) ions
 19. Bone repair material according to one of the claims 1 to 18, characterized in that said third component has a high ionic strength, preferably 0.15 M or higher.
 20. Bone repair material according to one of the claims 1 to 19, characterized in that said third component comprises a content of 0.1-1.0 w % of a hydrogel, preferably sodium hyaluronate.
 21. Bone repair material according to one of the claims 1 to 20, characterized in that it further comprises one or more drugs useful in the treatment of bone defects or bone diseases, in particular pharmaceutically or physiologically active substances
 22. Bone repair material according to one of the claims 1 to 21, characterized in that it further comprises an inorganic inhibitor for apatite dissolution and growth, preferably in the form of magnesium or pyrophosphate ions.
 23. Bone repair material according to one of the claims 1 to 22, characterized in that it further comprises an organic inhibitor for apatite dissolution and growth, preferably in the form of citrate ions, amino acids, peptides or proteins.
 24. Bone repair material according to one of the claims 1 to 23, characterized in that is in the form of a ready mixed puffy material.
 25. Bone repair material according to one of the claims 1 to 23, characterized in that said first and second component are in the form of a dry mixture to which the third component is to be added before use.
 26. Bone repair material according to claim 25, characterized in that the third component comprises blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells.
 27. Bone repair material according to one of the claims 1 to 23, characterized in that said second and third component are in the form of a nanocrystalline paste to which the first component is admixed before use.
 28. Bone repair material according to one of the claims 1 to 27, characterized in that said third component comprises partly or fully a fluid extracted from the patient without or with additional processing, preferably in the form of blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells.
 29. Bone repair material according to one of the claims 1 to 28, characterized in that said third component comprises cells with osteogenic potential that have been cultivated and/or differentiated prior to their use.
 30. Bone repair material according to claim 29, characterized in that said cells are embryonic stem cells, stem cells, bone marrow cells or osteoblasts.
 31. Bone repair material according to one of the claims 1 to 30, characterized in that it comprises a radiopacifier.
 32. Use of the bone repair material according to one of the claims 1-31 for the preparation of an agent for the treatment of osteoporosis or bone tumors.
 33. Use according to claim 32, characterized in that the mixture of the bone repair material is prepared in the operating room.
 34. Use according to claim 32 or 33, characterized in that blood, bone marrow, plasma, platelet-rich plasma or concentrated bone marrow cells are admixed as third component to a mixture of said first and second component. 